Continuous Counter-current Solvent Extraction of Magnesium and Calcium from Lithium-rich Brine

Fallah Fini, Mojtaba (2015)

Katso/Avaa
Master-Thesis-Mojtaba-Fallah-Fini.pdf (1.325Mb)
Lataukset: 


Diplomityö

Fallah Fini, Mojtaba
2015

Näytä kaikki kuvailutiedot
Julkaisun pysyvä osoite on
https://urn.fi/URN:NBN:fi-fe2015092413980

Tiivistelmä

Solvent extraction of calcium and magnesium impurities from a lithium-rich brine (Ca ~ 2,000 ppm, Mg ~ 50 ppm, Li ~ 30,000 ppm) was investigated using a continuous counter-current solvent extraction mixer-settler set-up. The literature review includes a general review about resources, demands and production methods of Li followed by basics of solvent extraction. Experimental section includes batch experiments for investigation of pH isotherms of three extractants; D2EHPA, Versatic 10 and LIX 984 with concentrations of 0.52, 0.53 and 0.50 M in kerosene respectively. Based on pH isotherms LIX 984 showed no affinity for solvent extraction of Mg and Ca at pH ≤ 8 while D2EHPA and Versatic 10 were effective in extraction of Ca and Mg. Based on constructed pH isotherms, loading isotherms of D2EHPA (at pH 3.5 and 3.9) and Versatic 10 (at pH 7 and 8) were further investigated. Furthermore based on McCabe-Thiele method, two extraction stages and one stripping stage (using HCl acid with concentration of 2 M for Versatic 10 and 3 M for D2EHPA) was practiced in continuous runs.
Merits of Versatic 10 in comparison to D2EHPA are higher selectivity for Ca and Mg, faster phase disengagement, no detrimental change in viscosity due to shear amount of metal extraction and lower acidity in stripping. On the other hand D2EHPA has less aqueous solubility and is capable of removing Mg and Ca simultaneously even at higher Ca loading (A/O in continuous runs > 1). In general, shorter residence time (~ 2 min), lower temperature (~23 °C), lower pH values (6.5-7.0 for Versatic 10 and 3.5-3.7 for D2EHPA) and a moderately low A/O value (< 1:1) would cause removal of 100% of Ca and nearly 100% of Mg while keeping Li loss less than 4%, much lower than the conventional precipitation in which 20% of Li is lost.
Kokoelmat
  • Diplomityöt ja Pro gradu -tutkielmat [13862]
LUT-yliopisto
PL 20
53851 Lappeenranta
Ota yhteyttä | Tietosuoja | Saavutettavuusseloste
 

 

Tämä kokoelma

JulkaisuajatTekijätNimekkeetKoulutusohjelmaAvainsanatSyöttöajatYhteisöt ja kokoelmat

Omat tiedot

Kirjaudu sisäänRekisteröidy
LUT-yliopisto
PL 20
53851 Lappeenranta
Ota yhteyttä | Tietosuoja | Saavutettavuusseloste