Effects of heat input on the mechanical properties of butt-welded high and ultra-high strength steels

Amraei, Mohsen; Ahola, Antti; Afkhami, Shahriar; Björk, Timo; Heidarpour, Amin; Zhao, Xiao-Ling (2019-08-09)

Linkki tietueeseen
Katso/Avaa
amraei_et_al_effects_of_post_print.pdf (4.339Mb)
Huom!
Sisältö avataan julkiseksi
: 10.08.2021

Post-print / Final draft

Amraei, Mohsen
Ahola, Antti
Afkhami, Shahriar
Björk, Timo
Heidarpour, Amin
Zhao, Xiao-Ling
09.08.2019

Engineering Structures

198

Elsevier

School of Energy Systems

https://doi.org/10.1016/j.engstruct.2019.109460
Näytä kaikki kuvailutiedot
Julkaisun pysyvä osoite on
http://urn.fi/URN:NBN:fi-fe2019082725782

Tiivistelmä

In this study, the mechanical properties of butt-welded thin plates made of S700, S960 and S1100 steels under various heat inputs (HI) are investigated. The gas metal arc welding (GMAW) process with two different levels of HI, and laser welding (LW) are implemented for this purpose. Fully automated welding process is employed to attain high quality and homogeneous weldments. Standard tensile tests of the butt-welded joints, together with micro-hardness measurements are conducted in this study. The microstructure of the heat affected zones (HAZ) of the weldments are closely examined using scanning electron microscopy (SEM). It was observed that while the fracture was occurred at the base materials of all S700 and S1100 weldments, the S960 suffered from failure at the HAZ which resulted in reduction of the joint’s strength and ductility. For all the studied steels, it was found that the joint’s ductility is highly dependent on HI values over the range of 0.3–1.4 kJ/mm for each welding pass. Though, the S1100 steel showed the best performance under welding HI with a moderate change in its mechanical properties and a stable microstructure after welding compared to S700 and S960.

Lähdeviite

Amraei, M., Ahola, A., Afkhami, S., Björk, T., Heidarpour, A., Zhao, X.-L. (2019). Effects of heat input on the mechanical properties of butt-welded high and ultra-high strength steels. Engineering Structures, vol. 198. DOI: 10.1016/j.engstruct.2019.109460

Kokoelmat
  • Tieteelliset julkaisut [438]
LUT-yliopisto
PL 20
53851 Lappeenranta
Ota yhteyttä | Lähetä palautetta | Tietosuoja
 

 

Tämä kokoelma

JulkaisuajatTekijätNimekkeetKoulutusohjelmaAvainsanatSyöttöajatYhteisöt ja kokoelmat

Omat tiedot

Kirjaudu sisäänRekisteröidy
LUT-yliopisto
PL 20
53851 Lappeenranta
Ota yhteyttä | Lähetä palautetta | Tietosuoja