Factors affecting the usability of aspen (Populus tremula) wood dried at different temperature levels
Kärki, Timo (2009-11-06)
Aineistoon ei liity tiedostoja.
Väitöskirja
Kärki, Timo
06.11.2009
Lappeenranta University of Technology
Acta Universitatis Lappeenrantaensis
Kuvaus
ei tietoa saavutettavuudesta
Tiivistelmä
In this dissertation the main aim was to study the usability of aspen wood in the mechanical wood processes, especially the factors that affect the usability of aspen wood, which is dried at different temperature levels.
The problematic of varying temperatures from level to another seem to have significant effects on distortions. According to the studies conducted, many practical solutions for drying of aspen timber can be made. European aspen sawn timber should be dried in relatively narrow widths, short lengths, edged and sawn pith free. The results achieved give an interesting view for the distortions of aspen wood between HT drying and heat treatment. The most significant result is that cupping seems to decrease when increasing temperature level from HT drying to heat treatment phase. The difference is significant. Other very obvious result is that bow and crook are increasing between these two temperature levels, bow significantly. Also the modelling gives a good background for this result since cupping is reduced by higher temperatures.
It can also be assumed that these distortions can be affected for example by sorting out the timber used to different moisture levels before drying. This could be a very simple solution for practical purposes. From practical point of view, it was also noted during the drying tests performed that the discoloration seem to be no problem for aspen boards dried in temperatures under 150 °C.
Altogether, this dissertation covers many interesting points of view of factors affecting distortions of wood in different temperature stages. Aspen as species in use of mechanical wood industries seems to be a species suitable for component production. According to the results, the best yield from aspen timber can be achieved in industry that can utilize relatively short components of sawn wood. Results achieved give a significant indication about the factors affecting distortions of wood at different temperature stages of drying, especially considering European aspen.
The problematic of varying temperatures from level to another seem to have significant effects on distortions. According to the studies conducted, many practical solutions for drying of aspen timber can be made. European aspen sawn timber should be dried in relatively narrow widths, short lengths, edged and sawn pith free. The results achieved give an interesting view for the distortions of aspen wood between HT drying and heat treatment. The most significant result is that cupping seems to decrease when increasing temperature level from HT drying to heat treatment phase. The difference is significant. Other very obvious result is that bow and crook are increasing between these two temperature levels, bow significantly. Also the modelling gives a good background for this result since cupping is reduced by higher temperatures.
It can also be assumed that these distortions can be affected for example by sorting out the timber used to different moisture levels before drying. This could be a very simple solution for practical purposes. From practical point of view, it was also noted during the drying tests performed that the discoloration seem to be no problem for aspen boards dried in temperatures under 150 °C.
Altogether, this dissertation covers many interesting points of view of factors affecting distortions of wood in different temperature stages. Aspen as species in use of mechanical wood industries seems to be a species suitable for component production. According to the results, the best yield from aspen timber can be achieved in industry that can utilize relatively short components of sawn wood. Results achieved give a significant indication about the factors affecting distortions of wood at different temperature stages of drying, especially considering European aspen.