Measurement and Improvement of Wet Paper Web Strength

Abstract

Various strength properties of paper are measured to tell how well it resists breaks in a paper machine or in printing presses. The most often measured properties are dry tensile strength and dry tear strength. However, in many situations where paper breaks, it is not dry. For example, in web breaks after the wet pressing the dry matter content can be around 45%. Thus, wet-web strength is often a more critical paper property than dry strength.

Both wet and dry strength properties of the samples were measured with a L&W tensile tester. Originally this device was not designed for the measurement of the wet web tensile strength, thus a new procedure to handle the wet samples was developed. The method was tested with Pine Kraft (never dried).

The effect of different strength additives on the wet-web and dry paper tensile strength was studied. The polymers used in this experiment were aqueous solution of a cationic polyamidoamine-epichlorohydrin resin (PAE), cationic hydrophilised polyisocyanate and cationic polyvinylamine (PVAm).

From all three used chemicals only Cationic PAE considerably increased the wet web strength. However it was noticed that at constant solids content all chemicals decreased the wet web tensile strength. So, since all chemicals enhanced solid content it can be concluded that they work as drainage aids, not as wet web strength additives. From all chemicals only PVAm increased the dry strength and two other chemicals even decreased the strength. As chemicals were used in strong diluted forms and were injected into the pulp slurry, not on the surface of the papersheets, changes in samples densities did not happen. Also it has to be noted that all these chemicals are mainly used to improve the wet strength after the drying of the web.