The intrinsic mechanisms of softwood fiber damage in brown stock fiber line unit operations Lappeenranta 2010

Abstract

The effects of pulp processing on softwood fiber properties strongly influence the properties of wet and dry paper webs. Pulp strength delivery studies have provided observations that much of the strength potential of long fibered pulp is lost during brown stock fiber line operations where the pulp is merely washed and transferred to the subsequent processing stages.

The objective of this work was to study the intrinsic mechanisms which maycause fiber damage in the different unit operations of modern softwood brown stock processing. The work was conducted by studying the effects of industrial machinery on pulp properties with some actions of unit operations simulated in laboratory scale devices under controlled conditions. An optical imaging system was created and used to study the orientation of fibers in the internal flows during pulp fluidization in mixers and the passage of fibers through the screen openings during screening. The qualitative changes in fibers were evaluated with existing and standardized techniques.

The results showed that each process stage has its characteristic effects on fiber properties: Pulp washing and mat formation in displacement washers introduced fiber deformations especially if the fibers entering the stage were intact, but it did not decrease the pulp strength properties. However, storage chests and pulp transfer after displacement washers contributed to strength deterioration. Pulp screening proved to be quite gentle, having the potential of slightly evening out fiber deformations from very deformed pulps and vice versa inflicting a marginal increase in the deformation indices if the fibers were previously intact. Pulp mixing in fluidizing industrial mixers did not have detrimental effects on pulp strength and had the potential of slightly evening out the deformations, provided that the intensity of fluidization was high enough to allow fiber orientation with the flow and that the time of mixing was short. The chemical and mechanical actions of oxygen delignification had two distinct effects on pulp properties: chemical treatment clearly reduced pulp strength with and without mechanical treatment, and the mechanical actions of process machinery introduced more conformability to pulp fibers, but did not clearly contribute to a further decrease in pulp strength. The chemical composition of fibers entering the oxygen stage was also found to affect the susceptibility of fibers to damage during oxygen delignification. Fibers with the smallest content of xylan were found to be more prone to irreversibledeformations accompanied with a lower tensile strength of the pulp. Fibers poor in glucomannan exhibited a lower fiber strength while wet after oxygen delignification as compared to the reference pulp. Pulps with the smallest lignin content on the other hand exhibited improved strength properties as compared to the references.