The Effects of Some Furnish and Paper Structure Related Factors on Wet Web Tensile and Relaxation Characteristics
Salminen, Kristian (2010-10-01)
Väitöskirja
01.10.2010
Lappeenranta University of Technology
Acta Universitatis Lappeenrantaensis
Julkaisun pysyvä osoite on
https://urn.fi/URN:ISBN:978-952-214-965-7
https://urn.fi/URN:ISBN:978-952-214-965-7
Tiivistelmä
The objective of this thesis was to identify the effects of different factors on the tension and tension relaxation of wet paper web after high-speed straining. The study was motivated by the plausible connection between wet web mechanical properties and wet web runnability on paper machines shown by previous studies.
The mechanical properties of wet paper were examined using a fast tensile test rig with a strain rate of 1000%/s. Most of the tests were carried out with laboratory handsheets, but samples from a pilot paper machine were also used. The tension relaxation of paper was evaluated as the tension remaining after 0.475 s of relaxation (residual tension).
The tensile and relaxation properties of wet webs were found to be strongly dependent on the quality and amount of fines. With low fines content, the tensile strength and residual tension of wet paper was mainly determined by the mechanical interactions between fibres at their contact points. As the fines strengthen the mechanical interaction in the network, the fibre properties also become important. Fibre deformations caused by the mechanical treatment of pulp were shown to reduce the mechanical properties of both dry and wet paper. However, the effect was significantly higher for wet paper.
An increase of filler content from 10% to 25% greatly reduced the tensile strength of dry paper, but did not significantly impair wet web tensile strength or residual tension. Increased filler content in wet web was shown to increase the dryness of the wet web after the press section, which partly compensates for the reduction of fibrous material in the web. It is also presumable that fillers increase entanglement friction between fibres, which is beneficial for wet web strength.
Different contaminants present in white water during sheet formation resulted in lowered surface tension and increased dryness after wet pressing. The addition of different contaminants reduced the tensile strength of the dry paper. The reduction of dry paper tensile strength could not be explained by the reduced surface tension, but rather on the tendency of different contaminants to interfere with the inter-fibre bonding. Additionally, wet web strength was not affected by the changes in the surface tension of white water or possible changes in the hydrophilicity of fibres caused by the addition of different contaminants.
The spraying of different polymers on wet paper before wet pressing had a significant effect on both dry and wet web tensile strength, whereas wet web elastic modulus and residual tension were basically not affected. We suggest that the increase of dry and wet paper strength could be affected by the molecular level interactions between these chemicals and fibres. The most significant increases in dry and wet paper strength were achieved with a dual application of anionic and cationic polymers. Furthermore, selectively adding papermaking chemicals to different fibre fractions (as opposed to adding chemicals to the whole pulp) improved the wet web mechanical properties and the drainage of the pulp suspension.
The mechanical properties of wet paper were examined using a fast tensile test rig with a strain rate of 1000%/s. Most of the tests were carried out with laboratory handsheets, but samples from a pilot paper machine were also used. The tension relaxation of paper was evaluated as the tension remaining after 0.475 s of relaxation (residual tension).
The tensile and relaxation properties of wet webs were found to be strongly dependent on the quality and amount of fines. With low fines content, the tensile strength and residual tension of wet paper was mainly determined by the mechanical interactions between fibres at their contact points. As the fines strengthen the mechanical interaction in the network, the fibre properties also become important. Fibre deformations caused by the mechanical treatment of pulp were shown to reduce the mechanical properties of both dry and wet paper. However, the effect was significantly higher for wet paper.
An increase of filler content from 10% to 25% greatly reduced the tensile strength of dry paper, but did not significantly impair wet web tensile strength or residual tension. Increased filler content in wet web was shown to increase the dryness of the wet web after the press section, which partly compensates for the reduction of fibrous material in the web. It is also presumable that fillers increase entanglement friction between fibres, which is beneficial for wet web strength.
Different contaminants present in white water during sheet formation resulted in lowered surface tension and increased dryness after wet pressing. The addition of different contaminants reduced the tensile strength of the dry paper. The reduction of dry paper tensile strength could not be explained by the reduced surface tension, but rather on the tendency of different contaminants to interfere with the inter-fibre bonding. Additionally, wet web strength was not affected by the changes in the surface tension of white water or possible changes in the hydrophilicity of fibres caused by the addition of different contaminants.
The spraying of different polymers on wet paper before wet pressing had a significant effect on both dry and wet web tensile strength, whereas wet web elastic modulus and residual tension were basically not affected. We suggest that the increase of dry and wet paper strength could be affected by the molecular level interactions between these chemicals and fibres. The most significant increases in dry and wet paper strength were achieved with a dual application of anionic and cationic polymers. Furthermore, selectively adding papermaking chemicals to different fibre fractions (as opposed to adding chemicals to the whole pulp) improved the wet web mechanical properties and the drainage of the pulp suspension.